报告题目：Design of 3D porous carbon monoliths and their supercapacitor properties

报告人：王延青

报告时间：5月12日（周五）下午

报告地点：嘉锡楼313

报告摘要：

Nitrogen-dopedporous activated carbon monoliths (NDP-ACMs) havelong been the most desirable materials for supercapacitors.Unique to the conventional templatebased Lewis acid/base activationmethods, herein, we report on a simple yet practicable novel approach to production of the three-dimensional NDP-ACMs(3D-NDP-ACMs). Polyacrylonitrile (PAN) containedcarbon nanotubes (CNTs) being pre-dispersed into tubular level of dispersions was used as the starting materialand the 3D-NDP-ACMs were obtained via a template-freeprocess. First, a continuouslymesoporous PAN/CNT based 3D monolith was established by using template-free temperature-induced phase separation (TTPS). Second, a nitrogen-doped 3D-ACMstructure was obtained via carbonization of thePAN/CNT based monolith. At last, 3D-NDP-ACMwithasurface area 613.8 m2/g anda pore volume 0.366cm3/g was obtained.A typical supercapacitorwith our3D-NDP-ACMsas the functioning electrodesgavea specific capacitance stabilized at 216 F/geven after 3000 cycles,demonstrated the advantageous

个人简介：

王延青，2011年获私费外国人留学生特待制度留学日本，2013年“国家优秀自费留学生奖学金”获奖者。2014年任北海道大学博士后研究员，2015年任东京大学特任研究员和东京大学华人科学技术促进会副会长，2016年以访问学者身份在美国宾夕法尼亚大学做研究。2015年入选日本学术振兴会（JSPS）外国人特别研究员，主持日本政府学术振兴会外国人青年学者特别研究基金项目。目前在东京大学做特任研究员。

从事碳纳米管石墨烯复合材料制备、分散技术研究及纳米技术应用等工作10年，开发出超级电容器储能材料，柔性触摸屏透明导电薄膜电极材料，环境净化用碳纳米管石墨烯光催化剂材料等。

发表论文26篇（SCI收录12篇，EI收录1篇），其中SCI论文第一作者或通讯作者9篇；授权发明专利10项；承担国家级和省级项目2项，主持日本政府青年学者研究项目一项，山东省科技进步一等奖主要完成人之一；参加国际会议14次，其中邀请报告1次，口头报告9次；为Chemical Communication，Physical Chemistry Chemical Physics (PCCP)和RSC Advances化学类期刊的审稿人。